Avaliação da eficácia de um gel de vedação no selamento da interface pilar/implante e na manutenção da pré-carga dos parafusos de retenção
| Autor: | Seloto, Camila Berbel. |
|---|---|
| Jazyk: | portugalština |
| Rok vydání: | 2017 |
| Předmět: | |
| Druh dokumentu: | Text |
| Popis: | Orientador: Wirley Gonçalves Assunção Banca: Paulo Henrique dos Santos Banca: Juliana Aparecida Delben Esse estudo avaliou a eficácia de um material de vedação na manutenção da pré-carga em parafusos de retenção bem como o desajuste pilar/implante e microinfiltração após ciclagem mecânica. Foram formados seis grupos (n=12) sendo, um grupo teste (T) e um grupo controle (C) para cada tipo de conexão pilar/implante (conexão hexagonal externa (HE) e pilares UCLA; conexão cone Morse (CM) e pilares UCLA; e conexão CM e pilares flexcone (FC)). Nos grupos testes (HET, CMT e FCT) foi aplicado um agente de vedação no parafuso de retenção, enquanto os grupos controle (HEC, CMC e FCC) foram mantidos da forma convencional. Todos os implantes foram embutidos em poliuretano e foram introduzido 0,7μl de Azul de Toluidina (AT) na porção mais profunda de cada um deles. Em seguida, os pilares foram posicionados sobre os implantes e parafusados com o torque recomendado pelo fabricante com auxílio de chave especifica e um torquímetro digital. Formados os corpos-de-prova, estes foram submetidos à ciclagem mecânica (1x106 ciclos), com frequência de 2Hz e carregamento oblíquo de 130N. As avaliações dos desajustes foram realizadas em um estereomicroscópio antes e após a ciclagem mecânica. Para verificar a capacidade de vedação do agente após a ciclagem mecânica foi desenvolvida uma curva padrão, na qual determinou-se a diluição de azul de toluidina (AT). Em seguida, os dados foram analisados em espectrofotômetro para a formação da curva padrão. Na sequência, os corpos-de-prova foram colocadas individu... (Resumo completo, clicar acesso eletrônico abaixo) This study evaluated the effectiveness of a sealing material in preload maintaining of retaining screws and the misfit on implant / abutment interface after mechanical cycling. It was formed six groups (n=12), being one test group (T) and other control group (C) for each type of abutment / implant connection (external hexagonal connection (EH) and UCLA abutments, Morse taper (MT) and UCLA abutments, and CM connection and flexcone (CF) abutments). In the test groups (EHT, MTT and CFT) a sealing agent was applied on the retention screw, whereas the control groups (EHC, MTC and CFC) were maintained in the conventional manner. All implants were embedded in polyurethane and into the deeper portion of each implant it was introduced 0.7 μl of Toluidine Blue (TB). After that, the abutments were screwed to the implants with the torque values recommended by the manufacturer with the aid of a specific wrench and a digital torque wrench. The specimens formed were submitted to mechanical cycling (1x106 cycles) with frequency of 2Hz and oblique loading of 130 N. The misfit evaluation were performed at a stereomicroscope before and after a mechanical cycling. In order to verify the gel sealing ability after the mechanical cycling a standard curve was performed to determine the blue toluidine (TB) dilution. Then the data obtained were analyzed in a spectrophotometer for a standard curve formation. Afterwards, the specimens were placed in vials containing 400μl of distilled water. The spectrophotometric analysis was performed at 8 different times (1, 3, 6, 24, 48, 72, 96 and 144 hours). Finally, measurements of final destorque values (post-cycling) were performed. The misfit data, destorque and dye release (sealing ability) were obtained and submitted to normality statistical tests and then analyzed by ANOVA and Tukey tests (α = 0.05). The ANOVA... Mestre |
| Databáze: | Networked Digital Library of Theses & Dissertations |
| Externí odkaz: |
|