Efeitos in vitro do fluoreto no potencial anticárie do laser de CO2 no esmalte dentário desmineralizado
| Autor: | Zancopé, Bruna Raquel, 1988 |
|---|---|
| Jazyk: | portugalština |
| Rok vydání: | 2012 |
| Předmět: | |
| Zdroj: | Repositório Institucional da UnicampUniversidade Estadual de CampinasUNICAMP. |
| Druh dokumentu: | masterThesis |
| Popis: | Orientador: Marinês Nobre dos Santos Uchôa Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba Made available in DSpace on 2018-08-19T22:26:32Z (GMT). No. of bitstreams: 1 Zancope_BrunaRaquel_M.pdf: 1896232 bytes, checksum: 1ad4dfeb1c62fb185eb83d4a91b915a4 (MD5) Previous issue date: 2012 O objetivo desse estudo foi avaliar se a irradiação com o laser de CO2 acentua a incorporação de flúor no esmalte dentário desmineralizado e avaliar se a irradiação com o laser de CO2 laser (?=10.6 ?m) com duas densidades de energia (11,3 J/cm² e 20,0 J/cm²), combinado com aplicação de flúor fosfato acidulado (FFA) pode inibir a progressão da lesão em esmalte dentário. 315 espécimes de esmalte cariado (EEC) foram utilizados em dois experimentos. No experimento 1, 150 EEC foram divididos em 10 grupos, as quais foram irradiados e combinados com uma aplicação de FFA antes, durante ou após irradiação. Em seguida, 50 espécimes tiveram a superfície avaliada pela microscopia eletrônica de varredura (MEV). A concentração de fluoreto de cálcio (CaF2) formada na superfície do esmalte foi determinada em 100 EEC (N=10, 10 grupos). Após analise de CaF2, uma nova análise MEV foi realizada em 50 espécimes. No experimento 2, 165 EEC (11 grupos, n=15) foram submetidos aos mesmos tratamentos do experimento 1 + grupo com apenas lesão de cárie. Após ciclagem de pH, o flúor nas soluções desmineralizadoras (desmin) e remineralizadoras (remin), microdureza e profundidade de lesão foram determinadas. Os resultados foram analisados pelo teste ANOVA e Tukey e pelo teste de Kruskal-Wallis e Student-Newman-Keuls ('alfa'=0.05). Os resultados mostraram que a irradiação isolada ou combinada com FFA acentua a formação de CaF2 na superfície do esmalte, a concentração de flúor nas soluções des-remin e inibe a progressão da lesão (p The aim of this study was to investigate if CO2 laser irradiation enhances fluoride uptake by demineralized dental enamel and to evaluate whether enamel lesion progression can be inhibited by CO2 laser (?=10.6 ?m) irradiation with two fluencies (11.3 J/cm² and 20.0 J/cm²) combined with acidulated phosphate fluoride (APF) application. 315 specimens of carious enamel (SCE) were used in two experiments. In experiment 1, 150 SCE were allocated to 10 groups, which were irradiated combined with one APF application performed either before, during or after irradiation. Following, 50 specimens had their surface examined for morphological changes by scanning electron microscopy (SEM). Fluoride as CaF2 formed on enamel surface was determined in 100 SCE (n=10, 10 groups). After CaF2 analysis, a new SEM analysis was performed in 50 specimens. In experiment 2, 165 SCE (11 groups, n=15) were submitted to the same treatments as in experiment 1 + a caries lesion only group. After pH cycling, fluoride in demineralizing (Demin) and remineralizing (Remin) solutions, microhardness and lesion depth were determined. The results were analyzed by ANOVA and Tukey test and by Kruskal-Wallis rank test and Student-Newman-Keuls test ('alpha'=0.05). The results showed that irradiation alone or combined with APF enhanced CaF2 formation on enamel surface, fluoride concentration in de-remin solutions and inhibited lesion progression (p?0.05). SEM observations showed evidences of melting, fusion and cracks. In conclusion, laser irradiation alone or combined with APF enhances CaF2 uptake and inhibits lesion progression on demineralized dental enamel. However no synergic effect was found Mestrado Odontopediatria Mestre em Odontologia |
| Databáze: | Networked Digital Library of Theses & Dissertations |
| Externí odkaz: |
|