S?ntese, caracteriza??o estrutural e diel?trica do Niobato de Ferro - FeNbO4

Autor: Nascimento J?nior, Crist?v?o Porciano do
Jazyk: portugalština
Rok vydání: 2017
Předmět:
Zdroj: Repositório Institucional da UFRNUniversidade Federal do Rio Grande do NorteUFRN.
Druh dokumentu: Doctoral Thesis
Popis: Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2018-02-21T21:47:55Z No. of bitstreams: 1 CristovaoPorcianoDoNascimentoJunior_TESE.pdf: 27666407 bytes, checksum: 4cdfec47679082d133ed4d3182cebe76 (MD5)
Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2018-02-23T20:41:29Z (GMT) No. of bitstreams: 1 CristovaoPorcianoDoNascimentoJunior_TESE.pdf: 27666407 bytes, checksum: 4cdfec47679082d133ed4d3182cebe76 (MD5)
Made available in DSpace on 2018-02-23T20:41:29Z (GMT). No. of bitstreams: 1 CristovaoPorcianoDoNascimentoJunior_TESE.pdf: 27666407 bytes, checksum: 4cdfec47679082d133ed4d3182cebe76 (MD5) Previous issue date: 2017-09-14
Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior (CAPES)
O niobato de ferro (FeNbO4) tem sido aplicado como foto?nodo em conversores de energia solar, sensores a g?s, tecnologias catal?ticas, fotodectoras e dispositivos eletr?nicos. No entanto, as descri??es de suas propriedades diel?tricas ainda s?o muito escassas. Foi preparado tr?s tipos de amostras a partir da moagem de alta energia (24h, 48h e 72h) dos precursores de: Nb2O5, ?-Fe e H2O. Depois do processo de moagem, os p?s resultantes da moagem passaram pelo processo de calcina??o por 4 horas a 1300?C. O tempo de calcina??o foi o mesmo para todas. Todas essas amostras passaram pela caracteriza??o diel?trica, mas antes elas foram prensadas a 1570 Kgf e sinterizadas ? 1000_C por 24 horas. As caracteriza??es estruturais das amostras foram realizadas atrav?s da difra??o de raios X, microscopia eletr?nica de varredura e fluoresc?ncia de raios X. Os resultados revelaram que a amostra mo?da por 24h tem 94,48 % de FeNbO4 e 5,52 % de Fe2O3, para 48h tem 97,82 % de FeNbO4 e 2,18 % de Fe2O3, para 72h tem 93,68 % de FeNbO4 e 6,32 % de Fe2O3. As propriedades diel?tricas foram analisadas atrav?s das curvas caracter?sticas I-V e da permissividade diel?trica complexa com rela??o a frequ?ncia. As curvas caracter?sticas obtidas mostraram um comportamento semelhante a dispositivos eletr?nicos semicondutores, pertencente a fam?lia dos tiristores. O nosso estudo trata de uma nova rota de s?ntese para obten??o do niobato de ferro. Os resultados indicam que as amostras t?m grande potencial para aplica??o em dispositivos eletr?nicos.
Iron niobate (FeNbO4) has been applied to the photodiode in solar energy converters, gas sensors, photo detectors, and electronic devices. However, a full description of your dielectric properties is still scarceness so. By using a high energy mill, they were prepared three kinds of samples (24, 48 and 72 hours) of the precursors of: Nb2O5, a-Fe e H2O. After milling process, the resultant powders were to calcinated for precisely 4 hours and in a temperature of 1 300 celsius. We used a hydraulic press about 1570 Kgf to produce the samples. Next, the samples were calcinated during a time considered the same for all of them and underwent to dielectric characterization. In the way to characterize the samples, the samples were submitted to X rays, scanning electronic microscopy and X rays uorescence. Results have been shown that samples milling by 24 hours, has 94.48% of FeNbO4 and 5.52% of Fe2O3, by 48h has 97.82% of FeNbO4 and 2,18% de Fe2O3, and by 72h has 93,68% of FeNbO4 and 6.32% of Fe2O3. Dielectric properties were analyzed through I-V characteristic curves and complex dielectric permitivity against frequency. The characteristic curves exhibited semiconductors electronic devices behave like thyristor class. Furthermore, the present work constitutes a fully new route to sintering iron niobate. The results indicate that the samples have great potential for application in electronic devices.