Autor: |
Wu Shangshu, Yu Zhou, Wang Junjie, Zhang Hanxin, Pei Chaoqun, Fu Shu, Fu Hao, Meng Jiajie, Feng Tao |
Jazyk: |
English<br />French |
Rok vydání: |
2019 |
Předmět: |
|
Zdroj: |
E3S Web of Conferences, Vol 79, p 02002 (2019) |
Druh dokumentu: |
article |
ISSN: |
2267-1242 |
DOI: |
10.1051/e3sconf/20197902002 |
Popis: |
The preparation of nanocrystalline aluminum (NC Al) was conducted in two steps. After the NC Al powder was synthesized by an Inert gas condensation (IGC) method in a helium atmosphere of 500 Pa, the NC Al powder was in-situ compacted into a pellet with a 10 mm diameter and 250 μm-300 μm thickness in a high vacuum (10-6 Pa-10-7 Pa) at room temperature. The NC Al samples were not exposed to air during the entire process. After the pressure reached 6 GPa, the relative density could reach 99.83%. The results showed that the grain size decreased with the increased of in-situ forming pressure. The NC Al samples present obvious ductile fracture, and the tensile properties were greatly changed with the increase of forming pressure. |
Databáze: |
Directory of Open Access Journals |
Externí odkaz: |
|