Salma Bougarrani, Preetam K. Sharma, Jeremy W. J. Hamilton, Anukriti Singh, Moisés Canle, Mohammed El Azzouzi, John Anthony Byrne |
| Jazyk: |
angličtina |
| Rok vydání: |
2020 |
| Předmět: |
|
| Zdroj: |
Nanomaterials, Vol 10, Iss 5, p 896 (2020) |
| Druh dokumentu: |
article |
| ISSN: |
2079-4991 |
| DOI: |
10.3390/nano10050896 |
| Popis: |
The determination of reaction pathways and identification of products of pollutants degradation is central to photocatalytic environmental remediation. This work focuses on the photocatalytic degradation of the herbicide Imazapyr (2-(4-methyl-5-oxo-4-propan-2-yl-1H-imidazol-2-yl) pyridine-3-carboxylic acid) under UV-Vis and visible-only irradiation of aqueous suspensions of CaxMnOy-TiO2, and on the identification of the corresponding degradation pathways and reaction intermediates. CaxMnOy-TiO2 was formed by mixing CaxMnOy and TiO2 by mechanical grinding followed by annealing at 500 °C. A complete structural characterization of CaxMnOy-TiO2 was carried out. The photocatalytic activity of the hetero-nanostructures was determined using phenol and Imazapyr herbicide as model pollutants in a stirred tank reactor under UV-Vis and visible-only irradiation. Using equivalent loadings, CaxMnOy-TiO2 showed a higher rate (10.6 μM·h−1) as compared to unmodified TiO2 (7.4 μM·h−1) for Imazapyr degradation under UV-Vis irradiation. The mineralization rate was 4.07 µM·h−1 for CaxMnOy-TiO2 and 1.21 μM·h−1 for TiO2. In the CaxMnOy-TiO2 system, the concentration of intermediate products reached a maximum at 180 min of irradiation that then decreased to a half in 120 min. For unmodified TiO2, the intermediates continuously increased with irradiation time with no decrease observed in their concentration. The enhanced efficiency of the CaxMnOy-TiO2 for the complete degradation of the Imazapyr and intermediates is attributed to an increased adsorption of polar species on the surface of CaxMnOy. Based on LC-MS, photocatalytic degradation pathways for Imazapyr under UV-Vis irradiation have been proposed. Some photocatalytic degradation was obtained under visible-only irradiation for CaxMnOy-TiO2. Hydroxyl radicals were found to be main reactive oxygen species responsible for the photocatalytic degradation through radical scavenger investigations. |
| Databáze: |
Directory of Open Access Journals |
| Externí odkaz: |
|