| Autor: |
YANG Xiaolin, MU Qinqin, CHEN Yonghui, YAN Qun |
| Jazyk: |
čínština |
| Rok vydání: |
2024 |
| Předmět: |
|
| Zdroj: |
Hangkong gongcheng jinzhan, Vol 15, Iss 5, Pp 120-126 (2024) |
| Druh dokumentu: |
article |
| ISSN: |
1674-8190 |
| DOI: |
10.16615/j.cnki.1674-8190.2024.05.12 |
| Popis: |
The turbine blades of aero-engines are subjected to cyclic high-low cycle loads in actual service environments，which is a typical high-low cycle micro motion fatigue condition. The frequent occurrence of fatigue fracture in turbine blades due to fretting fatigue seriously affects the safe operation of aero-engines. In order to study the high-low cycle fretting fatigue problems of hot end component materials，this paper designs an Inconel718 tenon connection simulation component and conducts high-low cycle composite fretting fatigue tests on it. Three different load/frequency experiment conditions were designed to compare the life distribution of the simulated parts under different conditions. The results show that high/low cycle load has significant influence on fretting fatigue life. With the increase of high/low cycle load or frequency，the fretting fatigue life of joints decreases. The test results have proven that the high-low cycle fretting fatigue test of the tenon joint structure effectively reproduces the actual service condition of turbine blades. By displaying the explicit finite element analysis，the predicted crack initiation location shows less dispersion compared to the experimental results. |
| Databáze: |
Directory of Open Access Journals |
| Externí odkaz: |
|