| Autor: |
D. Rozumek, Z. Marciniak |
| Jazyk: |
angličtina |
| Rok vydání: |
2017 |
| Předmět: |
|
| Zdroj: |
Frattura ed Integrità Strutturale, Vol 11, Iss 42, Pp 40-45 (2017) |
| Druh dokumentu: |
article |
| ISSN: |
1971-8993 |
| DOI: |
10.3221/IGF-ESIS.42.5 |
| Popis: |
The paper presents the fatigue test results including the cracks growth in the composite zirconium-steel subjected to oscillatory bending. Specimens of square cross-section without melted layer and with a melted layer were tested. In the specimens the net ratio of thickness of steel to zirconium layers was h1 : h2 = 2.5 : 1. It was observed that a higher fraction of the intermetallic inclusions near the interface increase the fatigue life. Two different interaction mechanisms between a crack and interface were observed |