Stitching Repair for Delaminated Carbon Fiber/Bismaleimide Composite Laminates

Autor: Jiantao Hua, Suli Xing, Shaohang An, Dingding Chen, Jun Tang
Jazyk: angličtina
Rok vydání: 2022
Předmět:
Zdroj: Polymers, Vol 14, Iss 17, p 3557 (2022)
Druh dokumentu: article
ISSN: 14173557
2073-4360
DOI: 10.3390/polym14173557
Popis: Due to the excellent mechanical properties and heat resistance, bismaleimide matrix composite materials have been widely used in aircraft. However, they are susceptible to low-energy impacts, such as bird hits, gravel, tools falling, etc., which can easily result in delamination. The delamination can significantly reduce the compression performance of composites and become a potential hazard for aircraft in service. In this paper, a stitching method developed from the Z-pin manufacturing process was proposed to repair delaminated laminates. Firstly, the delaminated area was stitched by fiber bundles that were pre-impregnated with glue. Then, the fiber bundles threading through the laminate become the pins after the curing process, thus producing the bridging effect between delaminated layers. As a result, the in-plane compressive properties of the laminate are enhanced. The parameters, including the size, number, and position of the stitching hole, for the stitching repair were optimized, and the factors affecting the repair effect were discussed through both finite element analysis and experiments. The results showed that for a carbon fiber/bismaleimide composite plate with a circular delamination roughly 30 mm in diameter, the in-plane compressive strength can be recovered from 54.45% to 84.23% of the pristine plate, and the modulus was fully recovered.
Databáze: Directory of Open Access Journals
Externí odkaz:
Nepřihlášeným uživatelům se plný text nezobrazuje