| Autor: |
Krassowski Eve, Jaeckel Bengt, Pander Matthias, Daßler David, Malik Stephanie |
| Jazyk: |
angličtina |
| Rok vydání: |
2023 |
| Předmět: |
|
| Zdroj: |
EPJ Photovoltaics, Vol 14, p 13 (2023) |
| Druh dokumentu: |
article |
| ISSN: |
2105-0716 |
| DOI: |
10.1051/epjpv/2023004 |
| Popis: |
It was previously shown that the Laser Enhanced Contact Optimization (LECO) Process is a promising boost for PERC and TOPCon cell manufacturing enhancement. In this contribution, a method is developed to assess the long-term stability of industrial LECO treated PERC cells in a module compound. Therefore, extended accelerated aging tests as well as outdoor measurements were performed on modules comprising LECO treated cells as well as untreated references. It is described, how data can be evaluated to separate typical, known aging and degradation effects from presumable LECO specific effects. The results of this work show that test modules comprising LECO treated cells did not show a different behavior in the accelerated aging or degradation compared to the reference. The same conclusion was found for thermal cycling and damp heat tests, both far in excess of IEC requirements, as well as in a sequential test sequence. In addition, their outdoor performance with local and integral measurements has been evaluated. We can conclude that for the tested PERC cells, aging and degradation effects appeared, but none of them could be attributed to the LECO process. Hence, improvements in the efficiency and/or yield on cell level due to LECO can be translated to the module or even system level considering typical aging and degradation behavior, independently of a prior LECO process. |
| Databáze: |
Directory of Open Access Journals |
| Externí odkaz: |
|
|
Nepřihlášeným uživatelům se plný text nezobrazuje |
K zobrazení výsledku je třeba se přihlásit.
|