Pottery Sand as Fine Aggregate for Preparing Alkali-Activated Slag Mortar

Autor: Zhenzhen Jiao, Ying Wang, Wenzhong Zheng, Wenxuan Huang
Jazyk: angličtina
Rok vydání: 2018
Předmět:
Zdroj: Advances in Materials Science and Engineering, Vol 2018 (2018)
Druh dokumentu: article
ISSN: 1687-8434
1687-8442
DOI: 10.1155/2018/3037498
Popis: Alkali-activated slag (AAS) mortars were prepared using pottery sand as a fine aggregate in a ratio of 1 : 1.75 using a blend of sodium silicate and NaOH as an alkaline activator at room temperature. The effects of sodium oxide content and silicate moduli on the setting time, fluidity, consistency, compressive strength, and drying shrinkage of different AAS mortars were determined. These results revealed that sodium oxide content and silicate modulus had little effect on the setting time and workability of the mortar; however, they did have a significant effect on their mechanical performance and drying shrinkage levels. All the AAS mortars exhibited faster setting times, better workability, and higher early and late compressive strength compared to traditional mortars. Optimum compressive strength was achieved at 93 and 123 MPa after 1 d and 28 d, respectively, using a silicate modulus of 1.2 and Na2O content of 8%. The microstructures of mortars were characterized using scanning electron microscopy with energy dispersive spectrometric (SEM/EDS) and mercury intrusion porosimetry (MIP). These results reveal that AAS mortars containing pottery sand as a fine aggregate may represent a promising building material with improved properties for use in the construction industry.
Databáze: Directory of Open Access Journals
Externí odkaz:
Nepřihlášeným uživatelům se plný text nezobrazuje