Self-polymerization epoxy/phthalonitrile (APPEN) pre-polymers were studied systematically, and then, gelation time and differential scanning calorimetry (DSC) were employed to investigate their curing behaviors. Taking advantage of orthogonal test analysis, the key factors that affected the co-polymerization of APPEN were defined and the appropriate pre-polymerization conditions were analyzed. A possible curing mechanism of APPEN was proposed. Then, the thermomechanical and mechanical properties of glass-fiber-reinforced APPEN laminates (APPEN/GF) prepared at 180 °C were analyzed to understand the cross-linked and aggregation structures. Fracture surface of the composite laminates was also investigated to reveal the copolymerization degree and the interfacial binding. The results indicated that APPEN/GF composites exhibit outstanding mechanical and thermomechanical properties (flexural strength, 712 MPa, flexural modulus, 38 GPa, and Tg > 185 °C). The thermal stability (T5% > 334 °C and IPDT reached 1482 °C) of APPEN/GF composites was also investigated to further reveal the copolymerization between epoxy resin and aminophthalonitrile, which may be beneficial to the application of epoxy-matrix-based composites in the field of high-performance polymer composites. |
| Databáze: |
Directory of Open Access Journals |
| Externí odkaz: |
|
|
Nepřihlášeným uživatelům se plný text nezobrazuje |
K zobrazení výsledku je třeba se přihlásit.
|