| Autor: |
Florian Kerber, Tilo Zienert, Konrad Kerber, Steffen Dudczig, Thomas Schemmel, Helge Jansen, Christos G. Aneziris |
| Jazyk: |
angličtina |
| Rok vydání: |
2023 |
| Předmět: |
|
| Zdroj: |
Open Ceramics, Vol 15, Iss , Pp 100424- (2023) |
| Druh dokumentu: |
article |
| ISSN: |
2666-5395 |
| DOI: |
10.1016/j.oceram.2023.100424 |
| Popis: |
Modern, high-quality steelmaking requires a comprehensive understanding of the behavior of refractories in service. Therefore, MgO–C refractories with different MgO grade were immersed once and twice into a steel melt at 1600 °C and 1680 °C, respectively, in a near-industrial steel casting simulator. The same materials were tested in static crucible melting tests. A coherent MgO layer containing low-melting phases and MgAl2O4 crystal-like structures formed on the specimens’ surface. The morphology and frequency of these structures were strongly related to the MgO grade of the specimens and the immersion procedure. A lower MgO grade caused an increased formation of low-melting phases, which contributed to a denser layer formed on the specimens’ surface, hampering gas diffusion and the formation of MgAl2O4 crystal-like structures. An increased steel melt temperature and the double immersion had a similar effect. Conversely, an excessive formation of MgO and/or MgAl2O4 was observed when the formed layer contained less low-melting phases. |
| Databáze: |
Directory of Open Access Journals |
| Externí odkaz: |
|