| Autor: |
Valeriy Dudko, Diana Yuzbekova, Sergey Gaidar, Sofia Vetrova, Rustam Kaibyshev |
| Jazyk: |
angličtina |
| Rok vydání: |
2022 |
| Předmět: |
|
| Zdroj: |
Metals, Vol 12, Iss 12, p 2177 (2022) |
| Druh dokumentu: |
article |
| ISSN: |
2075-4701 |
| DOI: |
10.3390/met12122177 |
| Popis: |
The effect of tempering on the mechanical properties, structure, and dispersion of secondary phase particles is studied in 0.4%C-2%Si-1%Cr-1%Mo-VNb steel. This steel austenitized at 900 °C with subsequent water quenching exhibits a yield stress of 1445 MPa and a lath martensite structure with MX particles of ~40 nm located in matrix and boundary M6C carbides of ~210 nm. Tempering in the temperature interval of 200–400 °C provides a yield stress of 1625 MPa due to the precipitation of ε-carbide and cementite within laths. The yield stress decreases to 1415 and 1310 MPa after tempering at 500 and 650 °C, respectively, due to the replacement of matrix carbides by boundary M23C6 carbide. A Charpy V-notch impact energy of ~12 J/cm2 is almost independent from tempering temperatures of up to 400 °C and increases up to ~33 J/cm2 after tempering at 650 °C due to decreased yield stresses and increased plasticity. |
| Databáze: |
Directory of Open Access Journals |
| Externí odkaz: |
|