Effect of nanosized bioactive glass addition on some physical properties of biodentine
| Autor: | Mehmet Burak Guneser, Tugce Yuca Ozturk, Asiye Nur Dincer Sahin, Betul Aycan Uysal, Ayce Unverdi Eldeniz |
|---|---|
| Jazyk: | angličtina |
| Rok vydání: | 2023 |
| Předmět: | |
| Zdroj: | Journal of Applied Biomaterials & Functional Materials, Vol 21 (2023) |
| Druh dokumentu: | article |
| ISSN: | 2280-8000 22808000 |
| DOI: | 10.1177/22808000231184059 |
| Popis: | The aim of this in vitro study was to investigate some physical properties of Biodentine (BD) (Septodont, France) that has been modified by adding nanosized bioactive glass (nBG) particles to it in different ratios. The cement was modified by adding 1% (7 mg) and 2% (14 mg) nBG powder to BD. BD was used as the control group in its commercial form. A total of 240 cement samples ( n = 80) were prepared according to the standard measurements for each test. Subsequently, tests to determine compressive strength, microhardness, initial setting time, and solubility of the samples were performed. The obtained data were statistically analyzed using one-way ANOVA and Tukey’s HDS tests, and the significance level was found to be 0.05. The compressive strength values of the samples modified with 1% and 2% nBG were higher than those of the unmodified BD; however, no statistically significant difference was found between them [BD + nBG (2 wt%) ⩾ BD+nBG (1 wt%) ⩾ control BD], ( p > 0.05). The microhardness values of the samples modified with 1% and 2% nBG were found to be significantly higher than those of the control group [BD + nBG (2 wt%) > BD+nBG (1 wt%) > control BD], p BD+nBG (1 wt%) >BD+nBG (2 wt%)], p |
| Databáze: | Directory of Open Access Journals |
| Externí odkaz: |
|