| Autor: |
Calvet, T., Solans, X., Mata, J. |
| Jazyk: |
English<br />Spanish; Castilian |
| Rok vydání: |
1999 |
| Předmět: |
|
| Zdroj: |
Boletín de la Sociedad Española de Cerámica y Vidrio, Vol 38, Iss 5, Pp 451-454 (1999) |
| Druh dokumentu: |
article |
| ISSN: |
0366-3175 |
| Popis: |
The preparation and characterization of mixed crystals with formula Li(NH4)1-xKxSO4 has been carried out. The characterization was by thermal analysis (DSC and ATD), X-ray diffraction on powder and single crystal samples at variable temperature and Raman spectroscopy at variable temperature. Two type of phases have been obtained: A solid solution with 0.94 < x < 1, with the same phases to those observed in the LiKSO4, but new phases, which are not shown by the LiKSO4, can be obtained according to the crystallization process. The second type of compounds have the formula Li(NH4)0.53K0.47SO4, with an hexagonal structure (a ≈ 3 aLiKSO4). This compound have a phase transition at 463K.En este trabajo se estudia la preparación y caracterización de las fases de los cristales mixtos de fórmula Li(NH4)1-xKxSO4. La caracterización se ha efectuado por análisis térmico con DSC y ATD, difracción de rayos-X sobre polvo cristalino con temperatura variable, difracción de rayos-X sobre muestra monocristalina a temperatura variable a fin de determina su estructura cristalina y por espectroscopia Raman a temperatura variable. Se han obtenido dos tipos de fases. Una solución sólida con 0.94 < x < 1 que presenta los mismos tipos estructurales que el LiKSO4, pero según el método de cristalización pueden aparecer nuevas fases que no presenta el LiKSO4. El segundo tipo de compuesto tiene por fórmula Li(NH4)0.53K0.47SO4, el cual presenta una estructura hexagonal con parámetro a ≈ 3 aLiKSO4. Este compuesto tiene por encima de la temperatura ambiente una sola transición a 463K. |
| Databáze: |
Directory of Open Access Journals |
| Externí odkaz: |
|