The high temperature oxidation behaviour in air of thermal sprayed CoNiCrAlY coatings obtained using a high frequency detonation gun was studied. The coatings have high cohesion and good substrate/coating adherence, being not significantly affected after cyclic oxidation in air under a maximum temperature of 1000°C. The thickness of the coating is not modified after the oxidation tests, and a thin and compact layer of alumina with a uniform thickness is created and as a result a good oxidation protection has been obtained.Se ha estudiado el comportamiento frente a la oxidación al aire a alta temperatura de un recubrimiento de CoNiCrAlY proyectado por detonación de alta frecuencia. Las capas obtenidas tras la proyección térmica en la atmósfera ambiental tienen una compacidad y adherencia muy altas y resultan muy poco afectadas tras una oxidación cíclica al aire bajo temperaturas máximas de 1000°C. En estas condiciones se mantiene el espesor de la capa protectora, dado que se genera espontáneamente una fina y compacta capa de alúmina, continua y de espesor homogéneo, que proporciona una protección eficaz contra la oxidación. |
| Databáze: |
Directory of Open Access Journals |
| Externí odkaz: |
|