Wenbin Gao, Yi Gu, Liangyu Chen, Hang Liang, Dongpo Wang, Mohsen Seifi, John J. Lewandowski |
| Jazyk: |
angličtina |
| Rok vydání: |
2023 |
| Předmět: |
|
| Zdroj: |
Journal of Materials Research and Technology, Vol 25, Iss , Pp 681-697 (2023) |
| Druh dokumentu: |
article |
| ISSN: |
2238-7854 |
| DOI: |
10.1016/j.jmrt.2023.05.255 |
| Popis: |
The influence of sensitization on the precipitation behaviour and environmentally assisted cracking (EAC) of AA5083 alloy with the –H128 temper have been investigated. 80 °C/500 h and 80 °C/1000 h sensitized specimens exhibit discontinuous Mg-rich precipitates along the grain boundaries, whereas almost continuous β′ phase is present along the grain boundaries in the 175 °C/100 h sensitized material. EAC susceptibility increases with increasing exposure time and elevated temperature. The relationship between nitric acid mass loss test (NAMLT) values and mechanical test results indicates that specimens with a NAMLT value greater than 25 mg/cm2 exhibit severe EAC. The test environment affects the degree of EAC due to the combined effects of anodic dissolution at the crack tip, hydrogen evolution, and hydrogen embrittlement. AA5083-H128 exhibits lower EAC susceptibility than AA5083-H131, likely due to its lower yield strength. High yield strength can produce more Mg-rich precipitates after sensitization, increase the constraint of the crack tip material and accelerate the diffusion rate of H atoms in the process zone of the crack tip. |
| Databáze: |
Directory of Open Access Journals |
| Externí odkaz: |
|