| Autor: |
Haoran Chen, Jiaxin Zhang, Robert Hill, Aylin Baysan |
| Jazyk: |
angličtina |
| Rok vydání: |
2024 |
| Předmět: |
|
| Zdroj: |
BMC Oral Health, Vol 24, Iss 1, Pp 1-12 (2024) |
| Druh dokumentu: |
article |
| ISSN: |
1472-6831 |
| DOI: |
10.1186/s12903-024-04061-8 |
| Popis: |
Abstract Background Root caries is preventable and can be arrested at any stage of disease development. The aim of this study was to investigate the potential mineral exchange and fluorapatite formation within artificial root carious lesions (ARCLs) using different toothpastes containing 5,000 ppm F, 1,450 ppm F or bioactive glass (BG) with 540 ppm F. Materials and methods The crowns of each extracted sound tooth were removed. The remaining roots were divided into four parts (n = 12). Each sample was randomly allocated into one of four groups: Group 1 (Deionised water); Group 2 (BG with 540 ppm F); Group 3 (1,450 ppm F) and Group 4 (5,000 ppm F). ARCLs were developed using demineralisation solution (pH 4.8). The samples were then pH-cycled in 13 days using demineralisation solution (6 h) and remineralisation solution (pH 7) (16 h). Standard tooth brushing was carried out twice a day with the assigned toothpaste. X-ray Microtomography (XMT) was performed for each sample at baseline, following ARCL formation and after 13-day pH-cycling. Scanning Electron Microscope (SEM) and 19F Magic angle spinning nuclear magnetic resonance (19F-MAS-NMR) were also performed. Results XMT results showed that the highest mineral content increase (mean ± SD) was Group 4 (0.09 ± 0.05), whilst the mineral content decreased in Group 1 (-0.08 ± 0.06) after 13-day pH-cycling, however there was evidence of mineral loss within the subsurface for Groups 1, 3 and 4 (p |
| Databáze: |
Directory of Open Access Journals |
| Externí odkaz: |
|
Full text from SpringerLink