| Popis: |
For many wood cutting processes, the interest of high-speed tool steels and tungsten carbides remains very important because of their good tool edge accuracy and easy grinding. The wear of high-speed steel and tungsten carbide is an important economic parameter. Wood extractives and silica have a potential adverse effect on tool wear. Rapid chemical wearing due to corrosion and mechanical wearing has been attributed to the presence of extractives and silica in wood and wood composites. This paper presents the wear characteristics of SKH51 high-speed steel and K10 tungsten carbide caused by extractive and abrasive materials present in the lesser-known Tapi-Tapi wood and wood composites of wood cement board, particleboard, MDF, and oriented strand board (OSB). Experimental results showed that wearing of the cutting tools tested was determined by extractives and silica contained in the wood and wood composites. Wood cement board, which is high in silica content, caused severe damage to the cutting edge of the high-speed steel. A corrosion/oxidation mechanism was found to contribute to the wear of SKH51 and K10 when cutting the Tapi-Tapi wood, MDF, particleboard, wood cement board, and OSB. The silica and extractives determined the abrasion and corrosion wear mechanism to a varying degree. |