| Autor: |
Angela M. Raba-Paéz, Ciro Falcony-Guajardo, Ivan Supelano-García, Miryam R. Joya |
| Jazyk: |
angličtina |
| Rok vydání: |
2020 |
| Předmět: |
|
| Zdroj: |
Applied Sciences, Vol 10, Iss 12, p 4257 (2020) |
| Druh dokumentu: |
article |
| ISSN: |
2076-3417 |
| DOI: |
10.3390/app10124257 |
| Popis: |
In order to improve the photocatalytic effect of Nb2O5, manganese from 1% to 10% was added by the polymeric precursor’s method. The samples obtained were subjected to different calcination temperatures from 400 to 700 °C. Characterization of the synthesized materials was performed by XRD, IR, Raman and Diffuse Reflectance Spectroscopy (DRS) spectroscopy, FE-SEM, Brunauer–Emmett–Teller (BET) method, Photoluminescence (PL) and Dynamic Light Scattering (DLS). Photocatalytic performance for degradation of Rhodamine B was also evaluated. The Rietveld refined X-Ray Diffraction (XRD) pattern of Nb2O5:Mn 1.0 wt.% (700 °C) sample was similar to that of the un-doped oxide, therefore indicating that Nb was replaced by Mn and, consequently, there are not significant variations in the oxide structure. The Nb2O5:Mn 10.0 wt.% (700 °C) sample has the lowest band gap energy. The specific surface area (SBET) PL value increased as manganese concentration increased. The Nb2O5:Mn 5.0 wt.% (700 °C) sample has an Eg of 3.15 eV and morphological and surface characteristics that made it an appropriate photocatalyst in the Rhodamine B degradation. The novelty of this work relies on the use of a small quantity of Mn ions as dopants leading to Nb2O5:Mn nanostructured particles without using any surfactant or other additives. |
| Databáze: |
Directory of Open Access Journals |
| Externí odkaz: |
|