| Autor: |
Jianning Wang, Wensheng Liu, Yunzhu Ma, Wentan Zhu, Baishan Chen, Lei Zhang, Kuokuo Bao, Chaoping Liang, Qingshan Cai |
| Jazyk: |
angličtina |
| Rok vydání: |
2023 |
| Předmět: |
|
| Zdroj: |
Journal of Materials Research and Technology, Vol 26, Iss , Pp 7284-7299 (2023) |
| Druh dokumentu: |
article |
| ISSN: |
2238-7854 |
| DOI: |
10.1016/j.jmrt.2023.09.053 |
| Popis: |
In order to understand the underlying material evolution during liquid phase sintering (LPS) process in hot isostatic pressing process (HIP), microstructure and mechanical properties of 90 W–Ni–Fe–Cu alloys fabricated at 1400 °C/150 MPa are examined systematically. For 90W-4.2Ni-1.8Fe–4Cu alloy, the typical LPS microstructure, which are spherical W grains uniformly surrounded by continuously distributed γ- (Ni, Fe, Cu) matrix phase with the lowest W–W contiguity of 0.31, is achieved successfully after HIP at 1400 °C/150 MPa. The excellent tensile strength reaches as high as 873 MPa with elongation of 17.3% due to the soft γ- (Ni, Fe, Cu) matrix phase. Moreover, the relationship between the microstructure parameters VM(1−CW−W) and elongation ε are established and analyze the association with dislocation motion in depth through electron backscattered diffraction (EBSD) characterization. To our best knowledge, the LPS behavior of tungsten alloy is in-situ revealed by high-temperature confocal scanning laser microscopy (HT-CSLM) for the first time. The current research provides a novel strategy for designing and fabricating powder metallurgy materials by LPS with pressure. |
| Databáze: |
Directory of Open Access Journals |
| Externí odkaz: |
|