Lignin/Poly(vinylpyrrolidone) Multifilament Fibers Dry‐Spun from Water as Carbon Fiber Precursors

Autor: Philipp Kreis, Erik Frank, Bernd Clauß, Volker Bauch, Heiko Stolpmann, Lisa Kuske, Tanja Schneck, Simon König, Michael R. Buchmeiser
Jazyk: angličtina
Rok vydání: 2024
Předmět:
Zdroj: Macromolecular Materials and Engineering, Vol 309, Iss 3, Pp n/a-n/a (2024)
Druh dokumentu: article
ISSN: 1439-2054
1438-7492
DOI: 10.1002/mame.202300296
Popis: Abstract The preparation of lignin‐based carbon fibers by dry spinning from aqueous solution followed by stabilization and continuous carbonization to endless yarns is reported. The influence of carbonization temperature and draw ratio on the morphology and mechanical properties of the final carbon fibers is investigated by single‐fiber testing, wide‐angle X‐ray scattering, scanning electron microscopy, and Raman spectroscopy. A draw ratio of 5% (1.05) with a carbonization temperature of 1400 °C leads to the best mechanical properties. The resulting multifilament carbon fibers have an average diameter between 10–12 µm, an average tensile strength of 1.30 ± 0.32 GPa, a Young's modulus of 101 ± 18 GPa, and an elongation at break of 1.31 ± 0.23%. The maximum Weibull strength (𝜎0) is 1.04 GPa with a Weibull modulus (m) of 5.1. The use of a water‐soluble system is economically advantageous; also, unlike melt‐spun lignin fibers, the dry‐spun precursor fibers can be thermally converted without any additional crosslinking step.
Databáze: Directory of Open Access Journals
Externí odkaz:
Nepřihlášeným uživatelům se plný text nezobrazuje