| Autor: |
Jiejun He, Lushu Wu |
| Jazyk: |
angličtina |
| Rok vydání: |
2022 |
| Předmět: |
|
| Zdroj: |
Metals, Vol 12, Iss 2, p 309 (2022) |
| Druh dokumentu: |
article |
| ISSN: |
2075-4701 |
| DOI: |
10.3390/met12020309 |
| Popis: |
A strengthening phenomenon has been demonstrated in the Mg–3Al–1Zn (AZ31) alloy after simultaneous annealing and loading at 180 °C. The microstructural analysis reveals that a few second-phase particles appear in the material after direct annealing at 180 °C for 20 h. However, a higher quantity of the second-phase particles (Al12Mg17) is observed in the alloy after simultaneous annealing and loading. Further, a high stress is observed to be more beneficial for the precipitation of the particles. It is speculated that the stress applied during annealing can provide a better condition for the nucleation of the precipitates. The enhanced extent of precipitates may play a significant role in preventing the dislocation gliding, thus, leading to a strengthening effect. The observed phenomenon may also provide a novel strategy for strengthening the magnesium alloys. |
| Databáze: |
Directory of Open Access Journals |
| Externí odkaz: |
|