Autor: |
Ahmad Zakiyuddin, Arya Abietta Irawan, Oknovia Susanti, Sri Harjanto |
Jazyk: |
angličtina |
Rok vydání: |
2020 |
Předmět: |
|
Zdroj: |
Archives of Metallurgy and Materials, Vol vol. 65, Iss No 3, Pp 1015-1018 (2020) |
Druh dokumentu: |
article |
ISSN: |
2300-1909 |
DOI: |
10.24425/amm.2020.133209 |
Popis: |
Mg-1.6Gd binary alloy was subjected to uniaxial warm rolling at a unidirectional and cross-sectional with a reduction ratio of 95% in order to observe the relationship between its microstructural changes to the degradation behavior. The warm rolling was performed at a temperature range of its recrystallization temperature, which were 400°C and 560°C, and a feed rate of 10 mm/min. Degradation behaviors of Mg-1.6Gd binary alloy was evaluated by means of potentiodynamic polarization and hydrogen evolution test in modified Kokubo’s SBF solution at temperature of 37 ± 1ºC. The lowest corrosion rate of 0.126 mm/year derived from potentiodynamic polarization test was showed by unidirectional-rolled specimen at temperature of 560 °C. Hydrogen evolution test results showed the lowest hydrogen gas formed during 24 hours of immersion was found on unidirectional-rolled specimen at temperature of 560°C with a rate of 0.268 cc/cm2/hours. While cross rolled specimens showed a high corrosion and hydrogen evolution rate of 20 mm/year and 0.28 cc/cm2/hours. |
Databáze: |
Directory of Open Access Journals |
Externí odkaz: |
|