Tetsuo NAGAMI, Toyokazu NOMOTO, Harue SUGIYAMA, Shoji TACHIKI, Ren SAKAMOTO, Toshiaki OHTA |
| Jazyk: |
angličtina |
| Rok vydání: |
2021 |
| Předmět: |
|
| Zdroj: |
Electrochemistry, Vol 89, Iss 4, Pp 363-369 (2021) |
| Druh dokumentu: |
article |
| ISSN: |
2186-2451 |
| DOI: |
10.5796/electrochemistry.21-00031 |
| Popis: |
We report detailed studies of capacity deterioration mechanism of Li[Ni1/3Co1/3Mn1/3]O2 (NCM) cathode after several numbers of cycling with the voltage range of 3.0–4.1 V/cell at 85 °C and after storage at charged states (3.7, 4.0 and 4.1 V/cell) at 70 °C for 150 days by soft X-ray absorption spectroscopy (XAS) and X-ray powder diffraction (XRD). Morphological changes were also observed by scanning electron microscopy (SEM).Ni, Co, and Mn L-edge XAS analysis revealed that Ni, a part of Co and no Mn were active for charge/discharge in the above-described voltage range. Only Ni L-edge XAS exhibited significant spectral changes by capacity deterioration. Ni mean valence at discharged state increased with the capacity deterioration rate of each sample either after storage test or after cycling test, which corresponds to the increase of the lattice constant ratio c/a, obtained by the XRD analysis. Chemically decomposed species on the NCM particle surfaces increased with capacity deterioration. Many cracks were observed in the SEM image of the sample after extended cycling. Crack generation, formation of the cubic spinel phase on the surface and deposition of decomposed species on the particles hamper the Li ion insertion to the cathode material at discharge, which is responsible for capacity deterioration. The crack generation is enhanced in case of the cycling test, while the deposition of decomposed species and the formation of the cubic spinel phase on the surface are more enhanced in case of the storage test. |
| Databáze: |
Directory of Open Access Journals |
| Externí odkaz: |
|