Influence of carbon content on the microstructure formation of duplex stainless steels Fe-25Cr-5Ni
| Autor: | Emanuelle Machado Amaral, Katia Cristiane Gandolpho Candioto, Angelo Fernando Padilha |
|---|---|
| Jazyk: | angličtina |
| Rok vydání: | 2021 |
| Předmět: | |
| Zdroj: | REM: International Engineering Journal, Vol 74, Iss 4, Pp 463-470 (2021) |
| Druh dokumentu: | article |
| ISSN: | 2448-167X 0370-4467 |
| DOI: | 10.1590/0370-44672021740011 |
| Popis: | Abstract This study evaluated the as-cast microstructure of three alloys based on Fe-25%Cr-5%Ni weight (wt.) composition whose carbon content is 0.02 wt.%, 0.12 wt.%, and 0.37 wt.%, respectively. Thermocalc was applied to predict the possible phases that could be formed during the cooling of each alloy and then the cross-sections of the ingots were characterized. The first alloy, with 0.02 wt.%C, presented a microstructure composed of ferrite and austenite, which was formed through solid-state precipitation. The second alloy, with 0.12 wt.%C, showed a microstructure formed by ferrite, austenite from the peritectic reaction (L + δ → γ) and M23C6 (M=Fe, Cr) carbide. Finally, the third alloy, with 0.37 wt.%C, exhibited a microstructure formed by dendrites of ferrite and austenite, also formed according to the peritectic reaction (L + δ → γ), with an M23C6 (M = Fe, Cr) and M7C3 (M = Fe, Cr) carbide network in the interdendritic regions. |
| Databáze: | Directory of Open Access Journals |
| Externí odkaz: |
|