For the fabrication of a peelable coating material that decomposes methyl paraoxone (MPO), a nerve agent simulant, self-crosslinkable waterborne polyurethanes (PUs) containing silane groups at the ends and a metal organic framework (UiO-66) were synthesized. UiO-66 dispersed PU solutions for spray coating were prepared by controlling the amount of silane in PU and the content of UiO-66. PUs with a large amount of silane (more than 7.2 wt.%) were easily gelated by adding UiO-66 because the solution was changed from neutral (pH = 7.3) to strongly acidic (pH = 2.5). Therefore, the silane content in PUs should be carefully controlled for the fabrication of composite films. When UiO-66 was added to the PU with a silane content of 2.7 wt.%, the reinforcing effect by UiO-66 was observed up to 15.3 wt.%, but a further increase in UiO-66 content decreased both the tensile strength and the elongation. The peel strength of the PU composite films on polyethylene (PET) and glass substrates decreased with increasing UiO-66 content, but their MPO conversion increased with increasing UiO-66 content. The PU composite film with 49.5 wt.% of added UiO-66 showed the MPO conversion of 63.2% and was easily peeled off from PET and glass substrates. |
| Databáze: |
Directory of Open Access Journals |
| Externí odkaz: |
|
|
Nepřihlášeným uživatelům se plný text nezobrazuje |
K zobrazení výsledku je třeba se přihlásit.
|