| Autor: |
Sung Yi, Nakyung Oh, Kyung-Eun Min, Je-Sik Shin, Cheolhee Kim |
| Jazyk: |
angličtina |
| Rok vydání: |
2023 |
| Předmět: |
|
| Zdroj: |
Applied Sciences, Vol 13, Iss 5, p 2876 (2023) |
| Druh dokumentu: |
article |
| ISSN: |
2076-3417 |
| DOI: |
10.3390/app13052876 |
| Popis: |
Polymer materials used in 3D printing exhibit degradation of material mechanical properties when exposed to thermal environments and thermal expansions can induce residual stresses in products or molds, which may result in dimensional instability and subsequent structural failures. In this study, based on linear thermo-viscoelastic principles, material degradation master curves, shift functions, and glass transition temperatures for four different polymers used for 3D printing techniques such as MultiJet Printing and Digital Lighting Process were measured by using a dynamic mechanical analyzer. Based on the single frequency test, the glass transition temperature was measured. In addition, dynamic measurements were carried out over a frequency range at isothermal condition and storage modulus vs. frequency curves were obtained. Then, the storage moduli curves measured at different temperatures were superposed into master curves using the frequency–temperature superposition principle and shift factors were calculated as a function of temperature. Subsequently, the complex moduli curves that were measured in the frequency were curve-fitted onto generalized Maxwell models by using the least squares method and the master curves of relaxation moduli at reference temperature were obtained. The effects of temperature, frequency, and time on dynamic moduli and relaxation behaviors of four polymers used for 3D printing were evaluated. Experimental results showed that Polymers C and D could be suitable to use at the service temperature above 100 °C and Polymer C was highly crosslinked and showed low modulus reduction after about a year. The master relaxation curves obtained through this process can be utilized to predict the long-term performance of polymer molds made by 3D printing at a given environmental condition. |
| Databáze: |
Directory of Open Access Journals |
| Externí odkaz: |
|