| Autor: |
Yasamin Hosseini, Ahmad Kermanpur, Fakhreddin Ashrafizadeh, Ahmad Keyvani |
| Jazyk: |
angličtina |
| Rok vydání: |
2023 |
| Předmět: |
|
| Zdroj: |
Journal of Materials Research and Technology, Vol 22, Iss , Pp 3387-3401 (2023) |
| Druh dokumentu: |
article |
| ISSN: |
2238-7854 |
| DOI: |
10.1016/j.jmrt.2022.12.185 |
| Popis: |
The effect of alumina (Al2O3) nanoparticles on the hot oxidation behavior of NiCoCrAlTaY coating is investigated. High velocity oxygen fuel (HVOF) technique was employed to deposit coatings on a single crystal CMSX-4 Ni-based superalloy. Different amounts of α-Al2O3 nanoparticles (3, 6 and 9 wt%) were added to NiCoCrAlTaY powder via a modified suspension route. By this modification, the Al2O3 nanoparticles were adhered on the surface of the atomized metallic NiCoCrAlTaY powders with a relatively uniform distribution. The composite powder was then sprayed on the superalloy substrate by an industrial HVOF route. The cyclic hot oxidation resistance of the coatings was evaluated at 1100 °C. Results showed that the coating with 6 wt% nano-Al2O3 experienced significantly better oxidation performance. The presence of nano-Al2O3 in the coating accelerated the formation of α-Al2O3 dense oxide layer and, thereby, delayed diffusion of other elements to the surface. Adding more Al₂O₃ nanoparticles up to 9 wt% led to an increase in porosity and surface roughness of the coating which decreased oxidation resistance. |
| Databáze: |
Directory of Open Access Journals |