Facundo Almeraya-Calderón, Jesús M. Jáquez-Muñoz, Erick Maldonado-Bandala, Jose Cabral-Miramontes, Demetrio Nieves-Mendoza, Javier Olgui-Coca, Luis Daimir Lopez-Leon, Francisco Estupiñán-López, Alejandro Lira-Martínez, Citlalli Gaona Tiburcio |
| Jazyk: |
angličtina |
| Rok vydání: |
2023 |
| Předmět: |
|
| Zdroj: |
Metals, Vol 13, Iss 9, p 1510 (2023) |
| Druh dokumentu: |
article |
| ISSN: |
2075-4701 |
| DOI: |
10.3390/met13091510 |
| Popis: |
Titanium alloys present superior electrochemical properties due to the generation of the TiO2 passive layer. The ability to generate an oxide passive layer depends on the anodized alloy. This work mainly studies the corrosion resistance of the alloys Ti-6Al-2Sn-4Zr-2Mo and Ti-6Al-4V anodized in NaOH and KOH at 1 M and 0.025 A/cm2 of current density. The electrochemical techniques were performed in a conventional three-electrode cell exposed to electrolytes of NaCl and H2SO4. Based on ASTM-G61 and G199, cyclic potentiodynamic polarization (CPP) and electrochemical noise (EN) techniques were used. The results indicated that Ti-6Al-2Sn-4Zr-2Mo anodized on NaOH presented a higher passivity range than anodized on KOH, relating to the high reactivity of Na+ ions. The former anodized alloy also demonstrated a higher passive layer rupture potential. In EN, the results showed that Ti-6Al-4V anodized in KOH presented a trend toward a localized process due to the heterogeneity of anodized porosity and the presence of V in the alloy. |
| Databáze: |
Directory of Open Access Journals |
| Externí odkaz: |
|