SERS OF BACTERIORHODOPSIN WITH OUT-DIFFUSED SILVER NANOISLANDS
| Autor: | H. Fabian, E. S. Piliugina, S. D. Chervinskii, A. K. Samusev, A. A. Lipovskii |
|---|---|
| Jazyk: | English<br />Russian |
| Rok vydání: | 2014 |
| Předmět: | |
| Zdroj: | Naučno-tehničeskij Vestnik Informacionnyh Tehnologij, Mehaniki i Optiki, Vol 14, Iss 5, Pp 18-22 (2014) |
| Druh dokumentu: | article |
| ISSN: | 2226-1494 2500-0373 |
| Popis: | We present the studies on surface-enhanced Raman spectroscopy (SERS) of bacteriorhodopsin in purple membranes using self-assembled silver nanoisland films for Raman signal enhancement. These metal island films were fabricated on soda-lime glass slides subjected to silver-sodium ion exchange in molten Ag0.05Na0.95NO3 at the temperature of 325°C for 20 minutes and subsequent treatment in hydrogen atmosphere at the temperature of 250°C for 10 minutes. The films typically consisted of 20–30 nm closely placed nanoislands. Being tested as SERS substrates for rhodamine 6G the nanoisland films gave the possibility to observe respective characteristic Raman lines from a dried drop of rhodamine 6G dissolved in water in the concentration of 10–6 M. Similarly fabricated substrates were used to obtain SERS spectra of bacteriorhodopsin in purple membranes dispersed in water, and Raman peaks at 1000–1020 cm–1, 1150–1220 cm–1 and 1530– 1570cm–1 were resolved. The substrates made it possible to register characteristic Raman peaks only for an order of magnitude lower concentration of bacteriorhodopsin in contrast to the virgin glass substrate, that is the enhancement of Raman signal was considerably less than for rhodomin 6G. This is supposed to be due to bacteriophodopsin molecules packing in patches, and it prevents bacteriophodopsin in purple membranes from penetration between the nanoislands where the local enhancement of the electric field of exciting light wave is maximal. |
| Databáze: | Directory of Open Access Journals |
| Externí odkaz: |
|