Electrochemically produced nano-TiO2-coated SiC membranes for photocatalytic water treatment: Preparation, characterization, and hydroxyl radical formation

Autor: Sarah Trepte, Claudia Kutzer-Schulze, Ulrike Langklotz, Mario Krug
Jazyk: angličtina
Rok vydání: 2024
Předmět:
Zdroj: Water Science and Technology, Vol 89, Iss 10, Pp 2783-2795 (2024)
Druh dokumentu: article
ISSN: 0273-1223
1996-9732
DOI: 10.2166/wst.2024.152
Popis: Photocatalytically active ceramic flat sheet membranes based on a nanostructured titanium dioxide (TiO2) coating were produced for photocatalytic water treatment. The nano-TiO2 layer was produced by a novel combination of magnetron sputtering of a thin titanium layer on silicon carbide (SiC) membranes, followed by electrochemical oxidation (anodization) and subsequent heat treatment (HT). Characterization by Raman spectra and field emission scanning electron microscopy proved the presence of a nanostructured anatase layer on the membranes. The influence of the titanium layer thickness on the TiO2 formation process and the photocatalytic properties were investigated using anodization curves, by using cyclovoltammetry measurements, and by quantifying the generated hydroxyl radicals (OH•) under UV-A irradiation in water. Promising photocatalytic activity and permeability of the nano-TiO2-coated membranes could be demonstrated. A titanium layer of at least 2 μm was necessary for significant photocatalytic effects. The membrane sample with a 10 μm Ti/TiO2 layer had the highest photocatalytic activity showing a formation rate of 1.26 × 10−6 mmol OH• s−1. Furthermore, the membranes were tested several times, and a decrease in radical formation was observed. Assuming that these can be attributed to adsorption processes of the reactants, initial experiments were carried out to reactivate the photocatalyzer. HIGHLIGHTS TiO2-coated membranes for photocatalytic wastewater treatment are promising to overcome the drawbacks of photocatalysis.; A novel coating method for ceramic flat sheet membranes with nanostructured TiO2 is described.; Nano-TiO2 coating is adhesive, permeable, has a high reaction surface, and shows favorable photocatalytic activity.; A decreasing photocatalytic effect with repeated membrane use is discussed.;
Databáze: Directory of Open Access Journals
Externí odkaz: