Five Layers Aurivillius Phases Pb2-xBi4+xTi5-xMnxO18: Synthesis, Structure, Relaxor Ferroelectric and Magnetic Properties
| Autor: | Zulhadjri Zulhadjri, B. Prijamboedi, A. A. Nugroho, N. Mufti, Ismunandar Ismu |
|---|---|
| Jazyk: | angličtina |
| Rok vydání: | 2013 |
| Předmět: | |
| Zdroj: | Journal of Mathematical and Fundamental Sciences, Vol 43, Iss 2 (2013) |
| Druh dokumentu: | article |
| ISSN: | 2337-5760 2338-5510 |
| DOI: | 10.5614/itbj.sci.2011.43.2.6 |
| Popis: | Synthesis of five layers Aurivillius phases, Pb2-xBi4+xTi5-xMnxO18 (0 "žT x "žT 1) were carried out by molten salts method using eutectic mixture of Na2SO4/K2SO4 salts (1:1 molar ratio) as the flux. The samples were characterized by X-ray diffraction powder and refined by Le Bail technique. The refinement results revealed that the samples with composition x = 0, 0.2, 0.4, and 0.6 formed five layers Aurivillius with the space group B2cb; however, the samples with x = 0.4 and 0.6 contained impurity as BiMnO3 and the additional phase of four layers Aurivillius (PbBi4Ti4O15) was also observed for x = 0.6. The samples with x = 0.8 and 1 resulted in two phases: four layers Aurivillius and BiMnO3. The dielectric properties of the Pb2-xBi4+xTi5-xMnxO18 show broad peaks with the temperature of the maximum of the dielectric constant (Tm) at temperature of 295, 295, 304, and 343"žaC at a frequency of 2 MHz for x = 0, 0.2, 0.4, and 0.6, respectively. The Tm of these samples is shift to the left with decreasing frequency as indication of relaxor ferroelectric behavior. The samples with x = 0.8 and 1 show anomaly at 514"žaC and 551"žaC which correspond to the transition phase of four layers Aurivillius. Magnetic properties for all samples containing Mn are paramagnetic. |
| Databáze: | Directory of Open Access Journals |
| Externí odkaz: |
|