FATIGUE PROPERTIES OF SPRING REINFORCES POLYMER GEARS
| Autor: | Hilal CAN, Faruk MENDİ, Muzaffer TOPÇU |
|---|---|
| Jazyk: | English<br />Turkish |
| Rok vydání: | 2005 |
| Předmět: | |
| Zdroj: | Pamukkale University Journal of Engineering Sciences, Vol 11, Iss 3, Pp 437-441 (2005) |
| Druh dokumentu: | article |
| ISSN: | 1300-7009 2147-5881 |
| Popis: | Failure of gears, occur surface pressure stress and fracture at base of teeth. For steel gears, it is known that process of carburizing increases fatigue strength. Internal stress on the surface increases of fracture fatigue strength. In this study fatigue properties of polypropylene gear reinforced with 1.2 mm wire diameter metallic springs was investigated. Extension springs were used as reinforcement element and placed into the mould and stretched before injection of polypropylene material into the mould. After injection of polypropylene, stretched springs were loosened in order to obtain pre-stressing. Fatigue tests were performed on the produced gear. Reinforcement increased the strength of gears. At result of experiments, pre-stressing increase in service life 12 times more than that of specimens without reinforcement. |
| Databáze: | Directory of Open Access Journals |
| Externí odkaz: |
|