Paolo Zampieri, Andrea Curtarello, Carlo Pellegrino, Emanuele Maiorana |
| Jazyk: |
angličtina |
| Rok vydání: |
2018 |
| Předmět: |
|
| Zdroj: |
Frattura ed Integrità Strutturale, Vol 12, Iss 43, Pp 90-96 (2018) |
| Druh dokumentu: |
article |
| ISSN: |
1971-8993 |
| DOI: |
10.3221/IGF-ESIS.43.06 |
| Popis: |
This note summarizes some recent investigation results on the behavior of corroded steel bolted joints under uniaxial fatigue loading. Fatigue test specimens, were made up using S355 structural steel plates joined together with preloaded M12 bolts of class 10.9 with a geometry that corresponds to the ?s = 112 MPa EC3 detail category. The accelerated corrosion process was accomplished using an electrolyte consisting of an aqueous 5% NaCl solution whereby the specimens were treated. In particular, during the corrosion process specimens were repeatedly immersed for 2 minutes in the electrolyte and then removed keeping them 60 minutes long in free air at 35 �C. An atmospheric corrosion in marine-industrial environment is wellrepresented through corrosion test. Fatigue loading tests and surface morphology measurement of uncorroded and corroded specimens were performed and the results were compared |
| Databáze: |
Directory of Open Access Journals |
| Externí odkaz: |
|