Abstract In this study, two bast fibers such as okra and jute were selected to manufacture composites taking polypropylene (PP) as matrix material by means of compression molding technique with maintaining 40% fiber content on the total weight of the composites. Investigation was done on tensile properties such as tensile strength (TS), tensile modulus (TM), elongation at break (EB%), bending properties such as bending strength (BS), bending modulus (BM) and impact properties like impact strength (IS) and hardness (Shore-A) of the composites. From analyzed data, it was found that Okra/PP composites showed very competitive mechanical properties to Jute/PP composites. Non-irradiated okra composite showed the value of TS, TM, BS, BM, IS and hardness to be 32.2 MPa, 602 MPa, 55.6 MPa, 3.6 GPa, 19.54 kJ/m2 and 95 (Shore-A), respectively, whereas that value for non-irradiated jute composite was 35.5 MPa, 629 MPa, 71.5 MPa, 4.5 GPa, 21.48 kJ/m2 and 96 (Shore-A), respectively. The composite samples were exposed to different intensities of gamma radiation (250‒1000 krad) at a dose rate of 330 krad/h and changes in mechanical properties were examined. Both irradiated composites (500 krad) showed significant improvement of mechanical properties compared to that of the non-irradiated composites. Maximum TS, TM, BS, BM and IS value were found to be 41.9 MPa, 685 MPa, 72 MPa, 4.7 GPa and 22.6 kJ/m2, respectively for irradiated okra composite and 45.3 MPa, 717 MPa, 88 MPa, 6.7 GPa and 24.3 kJ/m2, respectively for irradiated jute composite. Fourier transform infrared spectroscopy was used to identify the surface groups of the composites. Water absorption, degradation behavior of the composites under soil and heat medium were also performed. Degradation tests revealed that okra composite retained its original mechanical properties higher than that of jute composite. The morphology of the composites was inspected by scanning electron microscope. |
Full text from SpringerLink