Physio-Chemical Preparation of Slow-Release Potassium Fertilizers
| Autor: | Mohammad R. Alrbaihat, Ehab AlShamaileh, Aiman E. Al-Rawajfeh |
|---|---|
| Jazyk: | angličtina |
| Rok vydání: | 2022 |
| Předmět: | |
| Zdroj: | مجلة مركز بحوث التقنيات الاحيائية, Vol 16, Iss 2 (2022) |
| Druh dokumentu: | article |
| ISSN: | 1815-1140 2708-1370 |
| DOI: | 10.24126/jobrc.2022.16.2.663 |
| Popis: | Background: In this work, one of the novel types of slow-release fertilizers (SRF) consisting of kaolin as clay material and K2SO4 was synthesized through a mechanochemical process by grinding in a ball mill planetary model. Methodology: The test samples of different weight % from 25 to 75 of kaolin contents were milled for 2 h at fixed milling speeds of about 600 rpm to assess the integration of K2SO4 and to measure the liberation of K+ and SO4 2- ions into solution. The properties of the studied samples were characterized by Fourier transformation infrared spectrometry (FTIR), X-ray diffraction (XRD), thermal gravimetric analysis (TGA), and ion chromatography (IC). Incorporating K2SO4 into an amorphous kaolin structure using mechanochemistry is a green chemistry method that has been successfully applied. K+ content was measured in deionized water solution and the soil column leaching test was performed to determine the slow-release performance of the material. Results: The optimum released amount of K+ after 24 h was for (1:1 wt ratio) kaolin - K2SO4 samples that were 123.9 ppm at milling conditions at 600 rpm milling speed for 2 h. Conclusion: Indicating th |
| Databáze: | Directory of Open Access Journals |
| Externí odkaz: |
|