Production of M-type strontium hexaferrite magnetic powder with the high-pure magnetite concentrate via the ceramic process
| Autor: | Yujuan Zhou, Tao Jiang, Bin Xu, Yuming Lin, Min Zhang, Lanming Liu, Shouguo Zhong, Chengzhi Wei, Yufeng Chen, Yongbin Yang, Qian Li |
|---|---|
| Jazyk: | angličtina |
| Rok vydání: | 2022 |
| Předmět: | |
| Zdroj: | Journal of Asian Ceramic Societies, Vol 10, Iss 2, Pp 292-305 (2022) |
| Druh dokumentu: | article |
| ISSN: | 21870764 2187-0764 |
| DOI: | 10.1080/21870764.2022.2077280 |
| Popis: | The high-pure magnetite concentrate (HPMC) was studied for a substitution of iron scale to produce the magnetic powder of strontium hexaferrite via the conventional ceramic process in this work. The magnetic powder obtained under the optimum conditions had a magneto plumbite structure, which was confirmed by X-ray diffraction (XRD). Scanning electron microscope (SEM) depicted that ferrite grains were hexagon shaped and evenly distributed with an average particle size of about 1 μm. Furthermore, a comparison of magnetic powders separately produced with HPMC and iron scale was made by detecting the magnetic properties of their sintered magnets using a permanent magnetic measuring system. The results demonstrated that the HPMC magnetic powder had a superiority over iron scale magnetic powder, and it had fully achieved the level of Y30-1 product in China. In the final part, the economic feasibility of using HPMC for magnetic powder production was verified by the cost–benefit analysis. |
| Databáze: | Directory of Open Access Journals |
| Externí odkaz: |
|