In this study, the effects of electromigration on a solder/copper substrate due to temperature and current density stress were investigated. The copper–tin (Cu–Sn) film samples were subjected under a fixed current and various heating conditions (130 °C and 180 °C) and current densities (different cross-sectional areas). The micro-structural changes and intermetallic compound (IMC) formation were observed, and failure phenomena (brittle cracks, voids, bumps, etc.) on the structures of samples were discussed. The results showed that the IMC thickness increased as the temperature and current density increased. Moreover, it was found that the higher the temperature and current density was, the greater the defects that were observed. By adjusting the designs of sample structures, the stress from the current density can be decreased, resulting in reduced failure phenomena, such as signal delay, distortion, and short circuiting after long-term use of the material components. A detailed IMC growth mechanism and defect formation were also closely studied and discussed. |