Kaifeng Wang, Yang Chen, Nathaniel Findling, Frederic Charlot, Laurent Charlet, Jiliang Liu, Zhentao Zhang |
| Jazyk: |
angličtina |
| Rok vydání: |
2024 |
| Předmět: |
|
| Zdroj: |
npj Materials Degradation, Vol 8, Iss 1, Pp 1-10 (2024) |
| Druh dokumentu: |
article |
| ISSN: |
2397-2106 |
| DOI: |
10.1038/s41529-024-00444-y |
| Popis: |
Abstract The emergent secondary phases and surface altered layer (SAL) during the aqueous corrosion of borosilicate glass have a great impact on its chemical durability. However, the formation and evolution of these structures are still unclear. Here, by studying the borosilicate glass altered at 90 °C in pore water, the water in pore space between glass powders, the formation of secondary phases could follow two ways: 1. the consumption of aqueous ions forms analcime, zeolite, calcium silicate and barite at the surface of glass; 2. the reorganization of silica aggregates leads to smectite within the SAL. Small-angle X-ray scattering and cross-sectional scanning electron microscopy results show that the release of soluble elements and the formation of smectite within the SAL significantly increase the porosity of SAL. Furthermore, the layer containing smectite reorganizes inwardly and the crystallinity of smectite is gradually increased over time. The observations of transmission electron microscopy reveal that the dissolution of glass potentially goes through an interface-coupled dissolution-reprecipitation process. |
| Databáze: |
Directory of Open Access Journals |
| Externí odkaz: |
|
Full text from SpringerLink