| Autor: |
Ziyue Zhang, Jie Zhang, Xingyuan Zhao, Kai Wang, Xin Liu, Shiming Li, Sheming Jiang, Xuequn Cheng, Xiaogang Li, Qifu Zhang |
| Jazyk: |
angličtina |
| Rok vydání: |
2024 |
| Předmět: |
|
| Zdroj: |
Journal of Materials Research and Technology, Vol 31, Iss , Pp 2508-2516 (2024) |
| Druh dokumentu: |
article |
| ISSN: |
2238-7854 |
| DOI: |
10.1016/j.jmrt.2024.07.014 |
| Popis: |
Galvanized steel plates with Zn–Al–Mg coatings are extensively utilized due to their exceptional corrosion resistance. This study, focusing on the cracking behavior of coatings with varying Mg/Al ratios, was conducted using in-situ tensile tests on different samples. The influence of the Mg/Al ratio on the crack resistance of the sample coatings was systematically summarized. To elucidate this point, five types of Zn–Al–Mg coatings with varying Mg/Al ratios were prepared using the same galvanizing process and tensile testing performed using a scanning electron microscope equipped with in-situ tensile capabilities. Macroscopic digital image statistical techniques were employed to quantify the extent of coating cracking, demonstrating the impact of the Mg/Al ratio on the coatings' crack resistance. The findings suggest that an increase in the Mg/Al ratio deteriorates the crack resistance of the coating, while enhancing its hardness. Moreover, this research offers a novel perspective in evaluating the crack resistance of coatings by comparing the effects of different Mg/Al ratios. |
| Databáze: |
Directory of Open Access Journals |
| Externí odkaz: |
|