In this work, CaCu3Ti4O12 (CCTO) ceramics were prepared by solid state reaction at 900°C for 12 h and sintered at 1100°C during 3 h. The main phase detected through X-ray diffraction (XRD) was CCTO. Also, by means of Raman spectroscopy, it was observed a secondary phase rich in CuO. A dielectric constant higher than 13.000ε0 was obtained by Impedance spectroscopy measurements in the range between 25 to 106Hz. The value could be explained by the effect of dipolar and space charge polarization processes.En este trabajo se prepararon cerámicos basados en CaCu3Ti4O12 (CCTO) por reacción en estado sólido a 900°C y posterior sinterizado a 1100°C. Mediante difracción de rayos X (DRX) se comprobó la presencia de CCTO. A través de espectroscopía Raman se observó la presencia de una fase secundaria rica en CuO. Las mediciones de espectroscopía de impedancia demostraron que este material presenta una constante dieléctrica mayor a 13.000ε0 en el intervalo comprendido entre 25 y 106 Hz. Este valor es atribuido a la presencia de mecanismos de polarización de carga espacial y dipolar. |
| Databáze: |
Directory of Open Access Journals |
| Externí odkaz: |
|