| Autor: |
Roman Kolenak, Alexej Pluhar, Jaromir Drapala, Peter Gogola, Matej Pasak, Mikulas Sloboda |
| Jazyk: |
angličtina |
| Rok vydání: |
2024 |
| Předmět: |
|
| Zdroj: |
Applied Sciences, Vol 14, Iss 4, p 1504 (2024) |
| Druh dokumentu: |
article |
| ISSN: |
2076-3417 |
| DOI: |
10.3390/app14041504 |
| Popis: |
The aim of this study was to characterize a Zn-Mg type soldering alloy and direct soldering of SiC ceramics with a copper substrate. The Zn1.5Mg solder exerts a wider melting interval. The temperature of the eutectic reaction was 365 °C, and the liquidus temperature was 405 °C. The microstructure of the soldering alloy is comprised of a zinc matrix. Segregation of binary eutectics in the form of (Zn) + Mg2Zn11 lamellas occurred on the boundaries of Zn grains. Additionally, the presence of a MgZn2 magnesium phase was observed in the solder matrix. The SiC/solder bond was formed due to magnesium distribution from solder to the boundary with SiC ceramics, where magnesium reacts with silicon, which is infiltered in SiC ceramics. By a mutual interaction, a new Mg2Si phase is formed. An interaction between the molten zinc solder and Cu substrate occurred on the boundary of the Cu/substrate joint at the formation of a transition zone composed of two new phases, namely the γCu (Cu5Zn8) non-wettable phase type, approximately 30 µm wide, and a wettable (CuZn4) phase type ε, approximately 12 µm wide. The average shear strength of a combined SiC/Cu joint fabricated using Zn1.5Mg solder was 44 MPa. |
| Databáze: |
Directory of Open Access Journals |
| Externí odkaz: |
|