An Investigation into Mechanical Properties of Aluminum Matrix Nanocomposite Reinforced by Graphene–Boron Nitride Hybrid
| Autor: | Behzad Rahimzadeh, Maisam Jalaly, mehrdad Roshan |
|---|---|
| Jazyk: | angličtina |
| Rok vydání: | 2023 |
| Předmět: | |
| Zdroj: | Iranian Journal of Materials Science and Engineering, Vol 20, Iss 1, Pp 1-11 (2023) |
| Druh dokumentu: | article |
| ISSN: | 1735-0808 2383-3882 |
| Popis: | Considering the widespread use of aluminum composites in various industries and the emergence of nanomaterials such as graphene and boron nitrite (BN) with their unique properties, aluminum-based nanocomposite reinforced by the graphene-BN hybrid was fabricated at different percentages. For this purpose, the graphene-BN hybrid was prepared and subjected to wet milling along with the aluminum powder. The mechanical properties of the final nanocomposite which was consolidated using the spark plasma sintering (SPS) method were examined. Aluminum-based composite specimens containing 1 wt.% graphene–0 wt.% BN (AGB1), 0.95 wt.% graphene–0.05 wt.% BN (AGB2), 0.90 wt.% graphene–0.1 wt.% BN (AGB3), and 0.85 wt.% graphene–0.15 wt.% BN (AGB4) were fabricated and compared with non-reinforced aluminum (AGB0). The hardness values of 48.1, 51.1, 56.2, 54.1, and 43.6 Hv were obtained for AGB0, AGB1, AGB2, AGB3, and AGB4, respectively. Additionally, tensile strengths of these specimens were 67.2, 102.1, 129.5, 123.7, and 114.7 MPa, respectively. According to the results of the hardness and tensile tests, it was revealed that the AGB2 specimen had the highest tensile strength (93% higher than AGB0 and 27% higher than AGB1) and hardness (17% higher than AGB0 and 10% higher than AGB1). |
| Databáze: | Directory of Open Access Journals |
| Externí odkaz: |
|