Objectives: To evaluate the effect of ozone and two common denture cleansers on the surface hardness and bond strength of a silicone-based soft liner to acrylic denture base material. Materials and Methods: Sixty cylindrical specimens were fabricated using heat-cured poly-methyl methacrylate denture base resin. Three millimeters of the material was ground from the midsection and filled with the soft liner. The resilient liner specimens (n=40) used for the hardness test were 10 mm in diameter and 5 mm in height. Cylindrical and disc-shaped samples were randomly divided into four groups (37°C distilled water, Corega® tablets, 0.5% sodium hypochlorite (NaOCl), and a home ozone generator). To simulate six months of denture cleansing clinically, samples were placed in their cleanser once a day for six months according to the manufacturer’s instructions. All cylindrical specimens were placed under tension until failure in a universal testing machine at a crosshead speed of 5 mm/minute. For disc-shaped samples, hardness was measured using a Shore-A durometer. The results were analyzed using Kruskal-Wallis test, analysis of variance (ANOVA), and Tukey's post hoc test. Results: The mean tensile bond strength was not significantly different among the studied groups (P>0.05). The mean hardness in the ozone and Corega tablet groups was significantly lower than that of the control and NaOCl groups (P |
| Databáze: |
Directory of Open Access Journals |
| Externí odkaz: |
|