Impact of helium and hydrogen plasma exposure on surface damage and erosion of tungsten

Autor: Ryuichi Sakamoto, Elodie Bernard, Arkadi Kreter, Céline Martin
Jazyk: angličtina
Rok vydání: 2024
Předmět:
Zdroj: Nuclear Fusion, Vol 64, Iss 3, p 036008 (2024)
Druh dokumentu: article
ISSN: 1741-4326
0029-5515
DOI: 10.1088/1741-4326/ad1fab
Popis: The impact of helium plasma exposure on the tungsten surface damage structure development and erosion has been investigated by comparing the impact of hydrogen plasma exposure. Crystal orientation dependence of the undulating surface structure formation and erosion rate is observed on the plasma-exposed tungsten surface independently from the plasma species. The top surface of the plasma exposed tungsten has a tendency to {100} plane independently from the initial surface orientation. Although hydrogen and/or helium cause no erosion in tungsten under incident ion energy exposure conditions below the sputtering threshold, inevitable minute impurities, like oxygen, play an essential role in erosion, and significant erosion can be observed even at 30 eV.
Databáze: Directory of Open Access Journals