Internal stresses analysis on welded joint in Grade 91 steel under creep test: synchrotron DRX tests and modelling
| Autor: | Chen, Solenne Collomb Xiaolei, Tinnes, Jean-Philippe, Schenk, Thomas, Ferry, Olivier, Svetlana, Tsareva, Redjaïmia, Abdelkrim, Jacques, Alain |
|---|---|
| Rok vydání: | 2022 |
| Předmět: | |
| Druh dokumentu: | Working Paper |
| Popis: | The analysis and understanding of creep damage of Grade 91 steel welded joints is an important topic in the energy industry. Creep tests on welded joints were carried out at 600$^{\circ}$C, 100MPa and then interrupted at 0%, 10%, 30%, 50%, 80% of the expected life and after failure. Creep damage is characterised by cavity bands located exclusively in the core of the sample in the InterCritical Heat Affected Zone (ICHAZ). These samples were tested using \textit{in situ} synchrotron XRD along the welded joint under creep conditions for the different creep life time. The experimental results show a significant strain evolution and creep damage characteristic on the welded joint, with a local maximum at the Heat Affected Zone (HAZ). Following this, a finite element creep strain analysis was performed for comparison with the experimental results. Comment: 19 pages, 11 figures |
| Databáze: | arXiv |
| Externí odkaz: |
|