Кореляційний зв’язок між ефектами післядії за шорсткістю поверхонь металевого контртіла та карбопластика
| Autor: | Sirenko, H. O., Soltys, L. M., Skladanyuk, M. B. |
|---|---|
| Jazyk: | ukrajinština |
| Rok vydání: | 2016 |
| Předmět: | |
| Zdroj: | Physics and Chemistry of Solid State; Vol 16, No 2 (2015); 388-397 Фізика і хімія твердого тіла; Vol 16, No 2 (2015); 388-397 |
| Popis: | Regularities of change of isotropic roughness surfaces of steel 45 in friction and wear in a pair withpolymer composite has been researched. It has been detected that the topography of the conjugated metalsurface with polymer composite is the dominant factor in determining the value of wear of carbon-plastics atboth the start and in the process friction and wear when the metal surface roughness is created by thecomposite. It has been established that between after effects values for roughness of metal counterface andpolymer composite in friction and wear exists reliable linear relationship. Keywords: roughness, intensity of wear, isotropic surface, friction, composite polymer material, moments of spectral density. Досліджено закономірності зміни ізотропної шорсткості поверхонь сталі 45 під час тертя та зношування у парі з полімерним композитом. Виявлено, що топоґрафія спряженої з полімерним композитом металевої поверхні є домінуючим чинником у визначенні величини зносу карбопластика як на початку, так і в процесі тертя та зношування, коли шорсткість металевої поверхні твориться самим композитом. Встановлено, що між величинами ефектів післядії за шорсткістю металевого контртіла та полімерного композиту в процесі тертя та зношування існує надійний лінійний зв’язок. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|