The Composite Nickel Hydroxide / Activated Carbon as Electrode Material in the Battery Storage Devices
| Autor: | Khemiy, О. M., Yablon, L. S., Budzulyak, І. М., Morushko, O. V., Stubrov, Yu. Yu., Yaremiy, I. P. |
|---|---|
| Jazyk: | ukrajinština |
| Rok vydání: | 2016 |
| Zdroj: | Physics and Chemistry of Solid State; Vol 16, No 2 (2015); 355-359 Фізика і хімія твердого тіла; Vol 16, No 2 (2015); 355-359 |
| Popis: | The paper presents theresults of studies of the structure and electrochemical properties of composite β-Ni(OH)2/C. It is shown that the diffractograms composites intered β-Ni(OH)2/C in addition tope aks characteristic NiO,there is a broad diffraction peak at23°, which can be attributed to the activated carbon. Found that the composite electrode based onβ-Ni(OH)2/C has a specific capacity, which is almost 25 times higher than the capacity for the output of nickel hydroxide at a current of 1m A. Keywords: nickel hydroxide, activated carbon,thermogravimetry, X-ray analysis, galvanostatic and potentsio-dynamic methods, the accumulation of charge. У роботі представлено результати досліджень структури та електрохімічних властивостей композиту β-Ni(OH)2/C. Показано, що на дифрактограмах спеченого композиту β-Ni(OH)2/C крім піків характерних для NiO, спостерігається широкий дифракційний пік на 23°, який може бути віднесений до активованого вугілля. Виявлено, що електрод на основі композиту β-Ni(OH)2/С володіє питомою ємністю, що майже у 25 раз перевищує ємність для вихідного гідроксиду нікелю при струмі 1 мА. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|