Tezek Külü İkameli Çimento Harçlarının Mühendislik Özellikleri
| Autor: | ALTUNCI, Yusuf Tahir, ÖCAL, Cenk |
|---|---|
| Jazyk: | turečtina |
| Rok vydání: | 2020 |
| Předmět: | |
| Zdroj: | Volume: 8, Issue: 1 24-31 Bilecik Şeyh Edebali Üniversitesi Fen Bilimleri Dergisi |
| ISSN: | 2458-7575 |
| Popis: | In this study, engineering features of dung ash substituted cement mortars were investigated. Cow dung material was calcined at 400 °C and turned into dung ash, and the mixtures were prepared by substituting 0%, 2%, 4%, 6%, 8%, and 10% by weight instead of CEM I 42.5 R type cement. Setting times, expansions, spreading diameters, unit weight and bending, and compressive strengths of 2 and 28 days of prepared mixtures were determined. As a result, with the increase in the rate of substitution; it was determined that setting times were longer, spreading diameters, unit weight, bending, and compressive strengths decreased. In addition, it was determined that the substitution of dung ash up to 8% by weight instead of Portland cement did not affect the performance negatively in terms of the experiments. Bu çalışmada tezek külü ikameli çimento harçlarının mühendislik özellikleri incelenmiştir. İnekten elde edilen tezek malzemesi 400 0C de kalsine edilerek tezek külü haline getirilmiş ve CEM I 42.5 R tipi çimento yerine ağırlıkça %0, %2, %4, %6, %8 ve %10 oranlarında ikame edilerek karışımlar hazırlanmıştır. Hazırlanan karışımların; priz süreleri, genleşmeleri, yayılma çapları, birim hacim ağırlıkları ile 2 ve 28 günlük eğilme ve basınç dayanımları belirlenmiştir. Sonuç olarak ikame oranı artışı ile priz sürelerinin uzadığı, yayılma çaplarının, birim hacim ağırlıklarının, eğilme ve basınç dayanımlarının azaldığı belirlenmiştir. Ayrıca tezek külünün portland çimentosu yerine ağırlıkça %8 oranına kadar ikame edilmesinin yapılan deneyler açısından performansı olumsuz etkilemediği belirlenmiştir. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|